| SCP16GF is designed for use in rigid, flex, and rigid-flex circuit lamination processes. The specially formulated silicone rubber compounds KTCSR73 used in SCP press pads are designed for excellent thermal stability and compressibility in the lamination process. It is expect SCP press pads will be much more effective and stable than any other similar products. |
 |
| <Benefit> |
| ㆍExcellent stability at high temperature and high pressure. |
| ㆍUniform cushion property at high temperature. |
| ㆍLong available time in variety lamination process condition. |
| ㆍMinimization of decomposition silicone oil at high temperature and high pressure. |
| Pressing test at high temperature and high pressure. | Thermal resistance test |
| Test condition: Sample size(8cm X 8cm), Pressure setting(3.5Mpa), Pressing time(70minutes), Setting temperature(310℃) |
Test condition: Heating time(130minutes), Setting temperature(330℃) |
Decomposition silicone oil leakage a lot. Cushion property lost. |
Stickiness on the surface. Cushion Property lost. |
Decomposition silicone oil leakage slightly. Cushion property lost. |
Crack on the surface. Cushion property lost. |
Decomposition silicone oil leakage. Cushion Property lost. |
Crack on the surface. Cushion property lost. |
Decomposition silicone oil a little leakage . |
Almost no damage. |
<Typical Properties>
| Property | Unit | SCP16GF |
| Rubber Color | - | Red |
| Overall Thickness | mm | 1.6 |
| Substrate Type | 162 glass fabric | |
| Rubber hardness | Shore A | 73 ± 5 |
| Service Temperature | °C | 150 ~ 300 |
| Service Pressure | MPa | 0~10 |